摘要
塔筒金属材料在大气中的应力腐蚀会导致脆性断裂,从而对产生严重的后果。本文重点论述了应力腐蚀的几种腐蚀机理以及Cl-对应力腐蚀的影响,并介绍了应用较广的慢应力速率试验方法。
The stress corrosion in atmospheric environment will tower tube metal, and that will result in serious consequence lead to In this the brittle fracture of paper, several mechanism of stress corrosion and the influence of Cl to stress corrosion were discussed： and the slow strain rate tension test was introduced
出处
《环境技术》
2013年第1期5-8,共4页
Environmental Technology
基金
海上风力发电技术与检测国家重点实验室开放基金
关键词
大气腐蚀
应力腐蚀
Cl离子
慢应变速率试验
atmospheric corrosion
stress corrosion
Cl slow strain rate tension test