摘要
探讨了碳纤维(CF)表面镍金属的化学镀工艺,制备了镀镍碳纤维(NiCF),采用密炼工艺制备了ABS基体复合材料,研究了CF和NiCF含量对复合材料的导电性能及电磁屏蔽效能的影响。结果表明:采用化学镀的方法在碳纤维表面镀覆了金属镍,所形成的镀层均匀致密;镀覆时间为5min时,镀镍后的碳纤维电阻率降低两个数量级;复合材料电阻率随CF、NiCF含量的增加而逐渐减小;复合材料电磁屏蔽效能随CF、NiCF含量的增加而逐渐增加,当NiCF含量为25%(wt)(约13.3vol%)时,电磁屏蔽效能最高可达51dB。
This research investigated the metal-coating method of carbon fibers （CF）. Nickel-coated carbon fibers （NiCF） were fabricated by electroless plating, and ABS composites filled with CF and NiCF were prepared by kneading method. The influence of CF and NiCF contents on the electrical conductivity and electromagnetic shielding effectiveness of ABS based composites was studied. The results indicated that an even and intact nickel coating could be plated on carbon fibers under a suiltable pretreatment and plating conditions, and the electrical resistivity of CF decreased 2 orders of magnitude when the plating time was 5min. The electrical resistivity of composites decreased with CF and NiCF content increasing. The corresponding electromagnetic shielding effectiveness of composites increased as filler content increasing, and the value reached 51 dB for the composite containing 25wt% （13.3vol%） NiCF.
出处
《高分子通报》
CAS
CSCD
北大核心
2013年第2期46-50,共5页
Polymer Bulletin
基金
国家自然科学基金项目(21074016)
关键词
碳纤维
化学镀镍
电磁屏蔽
ABS
Carbon fiher； Electroless nickel plating
Electromagnetic interference
ABS