The aim was to investigate transformation behavior and transformation kinetics of an ultra-low carbon bai- nitic steel during continuous cooling. Continuous cooling transformation （CCT） curves of tested steel were measured by thermal dilatometer and metallographic structures at room temperature were observed by optical microscope. Then transformation kinetic equation of austenite to ferrite as well as austenite to bainite was established by analyzing the relationship of lnln]-l/（1--f）] and lnt in the kinetic equation on the basis of processed experimental data. Finally, the measured and calculated kinetic behaviors of the steel during continuous cooling were compared and growth pat- terns of transformed ferrite and bainite were analyzed. Results showed that calculated result was in reasonable agree- ment with the experimental data. It could be concluded that the growth modes of transformed ferrite and bainite were mainly one dimension as the Avrami exponents were between 1 and 2.
The aim was to investigate transformation behavior and transformation kinetics of an ultra-low carbon bai- nitic steel during continuous cooling. Continuous cooling transformation （CCT） curves of tested steel were measured by thermal dilatometer and metallographic structures at room temperature were observed by optical microscope. Then transformation kinetic equation of austenite to ferrite as well as austenite to bainite was established by analyzing the relationship of lnln]-l/（1--f）] and lnt in the kinetic equation on the basis of processed experimental data. Finally, the measured and calculated kinetic behaviors of the steel during continuous cooling were compared and growth pat- terns of transformed ferrite and bainite were analyzed. Results showed that calculated result was in reasonable agree- ment with the experimental data. It could be concluded that the growth modes of transformed ferrite and bainite were mainly one dimension as the Avrami exponents were between 1 and 2.