摘要
A series of single-phased Ca2Al2SiOT：EU2＋phosphors were synthesized by the solid-state reaction. Their structure and photoluminescence properties were investigated by the X-ray powder diffraction （XRD） and excitation and emission spectra in detail. The emission spectra of Ca2Al2SiO7：Eu2＋ phosphors consisted of blue and green band located at 419 and 542 nm, respectively. The relative intensities of the blue and green emission changed with Eu2＋ concentration and were sensitive to the excitation wavelength. The unique photoluminescence property originated from the 4f^7→4f65d transition of Eu2＋ at different energy levels, on which the effect of the crystal field strength was con- sidered to be tailed by adjusting the host composition.
A series of single-phased Ca2Al2SiOT：EU2＋phosphors were synthesized by the solid-state reaction. Their structure and photoluminescence properties were investigated by the X-ray powder diffraction （XRD） and excitation and emission spectra in detail. The emission spectra of Ca2Al2SiO7：Eu2＋ phosphors consisted of blue and green band located at 419 and 542 nm, respectively. The relative intensities of the blue and green emission changed with Eu2＋ concentration and were sensitive to the excitation wavelength. The unique photoluminescence property originated from the 4f^7→4f65d transition of Eu2＋ at different energy levels, on which the effect of the crystal field strength was con- sidered to be tailed by adjusting the host composition.
基金
Project supported by the Specialized Research Fund for the Doctoral Program of Higher Education of China (20115314120001)
the Special Program for National Program on Key Basic Research Project of China (973 Program) (2011CB211708)
the Foundation of Natural Science of Yunnan Province (2011FB022)