摘要
主要针对铝硅酸盐玻璃熔化温度高、黏度大、表面张力大、澄清困难等特点,通过试验研究,探讨了适合铝硅酸盐玻璃熔制的最佳澄清剂及澄清剂的比例,对铝硅酸盐玻璃的生产具有指导性的意义。
Aiming at the characteristics of aluminosilicate glass, such as high melting temperature, high viscosity,high surface tension and difficulty in refining, the refining agents used for aluminosilicate glass was investigated. The optimum refining agents, their optimal amount and ratio, and proper application method are described. They are very helpful for the refining process of aluminosilicate glass.
出处
《玻璃与搪瓷》
CAS
2012年第6期1-5,共5页
Glass & Enamel
关键词
铝硅酸盐玻璃
澄清剂
芒硝
硝酸钠
氧化铈
aluminosilicate glass
refining agent
sodium sulphate
sodium nitrate
cerium oxide