The aim of this work was to evaluate the catalytic properties of a Ru promoted Co/SBA-15 catalyst for Fischer-Tropsch synthesis （FTS）. The Ru promoted Co/SBA-15 catalyst was prepared by wet impregnation method and was characterized by X-ray diffraction, X-ray energy dispersion spectrophotometer, N2 adsorption-desorption, temperature-programmed reduction and transmission electron microscopy. The Fischer-Tropsch synthesis using the catalyst was carried out to evaluate the catalyst activity and its effect on FTS product distribution. The synthesis was carried out in a slurry reactor operating at 513 K, 20 atm, CO ： H2 molar ratio of 1 ： 1. X-ray diffraction showed that the calcined cobalt catalyst did not modify the structure of SBA-15, proving that Co was present in the form of Co3O4 in the catalyst. The addition of cobalt in SBA-15 decreased the specific superficial area of the molecular sieve. Fischer-Tropsch synthesis activity and C5＋ hydrocarbon selectivity increased with the addition of Ru. The increases in activity and selectivity were attributed to the increased number of active sites resulting from higher reducibility and the synergetic effect of Ru and Co. Ru/Co/SBA-15 catalysts showed moderate conversion （40%） and high selectivity towards the production of C5＋ （80 wt%）.
The aim of this work was to evaluate the catalytic properties of a Ru promoted Co/SBA-15 catalyst for Fischer-Tropsch synthesis （FTS）. The Ru promoted Co/SBA-15 catalyst was prepared by wet impregnation method and was characterized by X-ray diffraction, X-ray energy dispersion spectrophotometer, N2 adsorption-desorption, temperature-programmed reduction and transmission electron microscopy. The Fischer-Tropsch synthesis using the catalyst was carried out to evaluate the catalyst activity and its effect on FTS product distribution. The synthesis was carried out in a slurry reactor operating at 513 K, 20 atm, CO ： H2 molar ratio of 1 ： 1. X-ray diffraction showed that the calcined cobalt catalyst did not modify the structure of SBA-15, proving that Co was present in the form of Co3O4 in the catalyst. The addition of cobalt in SBA-15 decreased the specific superficial area of the molecular sieve. Fischer-Tropsch synthesis activity and C5＋ hydrocarbon selectivity increased with the addition of Ru. The increases in activity and selectivity were attributed to the increased number of active sites resulting from higher reducibility and the synergetic effect of Ru and Co. Ru/Co/SBA-15 catalysts showed moderate conversion （40%） and high selectivity towards the production of C5＋ （80 wt%）.
基金
supported by the Coordenao de Aperfeioamento de Pessoal de Nível Superior(CAPES)and Petrobras