摘要
制备了一种多层有机电致发光器件,其结构为ITO/m-MTDATA(45nm)/NPB(10nm)/DPVBi(15nm)/C545T(Xnm)/DCM2(Ynm)/Bhen(20nm)/Alq3(15nm)/LiF(1.0nm)/Al(200nm)。荧光材料C545T和DCM2以亚单层的方式插入蓝光发光层DPVBi后,通过改变双亚单层的厚度,观察器件性能的变化。当X/Y=0.05nm/0.05nm时,器件在8V的电压下最大发光效率是5.50cd/A,在13V的电压下最大的亮度是12 980cd/m2。研究了亚单层厚度的变化对器件的发光亮度、效率和光谱的影响。从实验结果中对比分析了三种器件的电流密度-电压曲线、亮度-电压曲线、电致发光光谱图和色坐标。从其中总结规律,对有机发光器件制作有一定的指导作用。
One kind of organic light-emitting diodes（OLED） with the multilayer structure of ITO / m-MTDATA（45 nm） / NPB（10 nm） / DPVBi（15 nm） / C545T（X nm） / DCM2（Y nm） / Bhen（20 nm） / Alq3（15 nm）/LiF（1.0 nm）/Al（200 nm） was prepared.The fluorescent materials of C545T and DCM2 as dual sub-monolayers were inserted into the blue luminous layer of DPVBi.By changing the thickness ratio of X/Y,the performance of the devices was tested.It is shown that as X/Y is 0.05 nm/0.05 nm,the maximum luminous efficiency is 5.50 cd/A at 8 V and the highest brightness is 12 980 cd/m2 at 13 V.The effects of different thickness of sub-monolayers on the luminous efficiency,brightness and spectrum are analyzed.
出处
《半导体光电》
CAS
CSCD
北大核心
2012年第5期632-635,共4页
Semiconductor Optoelectronics
基金
福建省自然基金资助项目(2011J01359)
福建省教育厅JK类科研项目(JK2011043)
泉州市科技局基金项目(2011G16)