摘要
研究了经高温高压渗氢后 ,30 9L 和 347L 不锈钢堆焊层短裂纹的低频疲劳特性。并用 da/d N=C(ΔJ) n 计算了裂纹扩展速度和门槛值。结果表明 ,经热渗氢后 ,30 9L和 347L堆焊层裂纹扩展的门槛值 (ΔJth)分别从空气中的 196× 10 - 6 MN/m和 35 5× 10 - 6 MN/m,下降为 144× 10 - 6 MN/m和 2 5 2× 10 - 6 MN/m;da/d N～ ΔJ曲线也比空气中的向左移 ,提高了裂纹扩展速度。
The characteristics of low frequency fatigue for the weld overlay cladding of 309L and 347L in hgdrogen at high temperature and pressure have been investigated. The crack propagation rate and threshold value are calculated using d a /d N=C (Δ J ) n. The rsults showed that:for 309L:(d a /d N ) Ⅰ=109.9×10 4(Δ J ) 4.27 m/c;(d a /d N ) Ⅱ=79.7×10 -8 (Δ J ) 0.123 m/c;Δ J th =144×10 -6 MN/m.for 347L:(d a /d N ) Ⅰ=28.18×10 5(Δ J ) 4.53 m/c;(d a /d N ) Ⅱ=89.06×10 -8 (Δ J ) 0.22 m/c;Δ J th =252×10 -6 MN/m. The hydrogen increased obviously the fracture sensiti vity, compared with pure mechanical fatigue in air.