摘要
Cu, As, Sb and Bi in copper electrolyte could be efficiently removed by reducing with SO2 followed by evaporative crystallization. As2O3 and CuSO4·5H2O were obtained after crystallized product was treated by dissolution, oxidation, neutralization, sedimentation, filtration and evaporative crystallization. The removal rates of Cu, As, Sb and Bi are 87.1%, 83.9%, 21.0% and 84.7%, respectively, when As （Ⅴ） in copper electrolyte is fully reduced to As （Ⅲ） by SO2, and the H2SO4 in concentrated copper electrolyte is 645 g/L. The removal rate of As is 92.81% when 65 g crystallized product is dissolved in 200 mL water at 30 ℃. The CuSO4·5H2O content is 98.8% when the filtrate is purified under the conditions that n（Fe）：n（As） is 1.2, the dosage of H2O2 is 19 times the stoichiometric needed, temperature is 45 ℃, time is 40 min, pH is 3.7, and then is evaporation crystallized.
经二氧化硫还原、蒸发结晶,使铜电解液中铜、砷、锑和铋得到有效去除。结晶产物经过溶解、氧化、中和、沉淀、过滤和蒸发结晶,得到三氧化二砷和硫酸铜。当采用SO2将铜电解液中As(Ⅴ)充分还原为As(Ⅲ),并加热蒸发浓缩铜电解液中硫酸浓度至645g/L时,铜电解液中铜、砷、锑和铋的去除率分别为87.1 %,83.9 %,21.0 %和84.7%。在温度30℃,将65g结晶产物溶于200mL自来水时,砷的去除率为92.81%。将所得滤液在如下条件下净化:n(Fe):n(As)为1.2,双氧水为理论用量的19倍,氧化温度为45℃,氧化时间为40min,终点pH为3.7,净化后蒸发浓缩结晶,所得硫酸铜溶液中硫酸铜含量达到98.8%。