Superhydrophobic aluminum surfaces with a high water contact angle and low sliding angle on aluminum plate substrate were fabricated by means of surface etching with sodium hydroxide under ultrasonic bathing and then modification with fluorosilane. Scanning electron microscopy（SEM） showed a honeycomb-like structure on aluminum substrate surface after etching under ultrasonic bathing. And the surface was rendered from superhydrophilicity to superhydrophobicity after further modification with fluorosilane.
Superhydrophobic aluminum surfaces with a high water contact angle and low sliding angle on aluminum plate substrate were fabricated by means of surface etching with sodium hydroxide under ultrasonic bathing and then modification with fluorosilane. Scanning electron microscopy（SEM） showed a honeycomb-like structure on aluminum substrate surface after etching under ultrasonic bathing. And the surface was rendered from superhydrophilicity to superhydrophobicity after further modification with fluorosilane.