双甘膦修饰磁性四氧化三铁纳米微球吸附DNA的研究被引量：1

Adsorption of DNA by PMIDA Modified Magnetic Iron Oxide Nanospheres

下载PDF

导出

摘要用双甘膦(PMIDA)修饰磁性四氧化三铁纳米微球(MNP)并负载Zn2+制得了PMIDA-Zn2+修饰磁性微球吸附剂。考察了吸附溶液的pH值、离子强度、吸附时间、吸附温度等因素对DNA吸附的影响。结果表明,当吸附剂用量为10mg、pH值为5.0、离子强度(NaCl浓度)为2.0mol.L-1、吸附时间为20min、吸附温度为35℃时,吸附率可达80%,吸附容量为21mg.g-1。被吸附的DNA用3.5%的氨水能完全洗脱。将PMIDA-Zn2+修饰磁性微球用于玉米DNA的提取,所得DNA纯度较高,效果令人满意。 PMIDA Modified magnetic iron oxide nanospheres, which were chelated with Znz＋, were ob- tained. The effects of adsorption conditions including adsorption solution pH value, ionic strength, adsorption time and adsorption temperature on DNA adsorption were investigated. The results showed that the adsorption rate and the adsorption capacity could reach up to 80% and 21 mg·L^-1,respectively, when the adsorbent dos- age was 10 mg,the solution pH value was 5.0,ionic strength （NaC1 concentration） was 2.0 tool·L^-1 ,adsorp- tion time was 20 min and adsorption temperature was 35 ℃. The adsorbed DNA could be completely eluted from the magentic nanospheres by 3.5 % ammonia solution. When the modified microspheres were applied to extrac- ting DNA from corn flour,the results were satisfactory with high-purified DNA.

作者孙群李步海

机构地区中南民族大学化学与材料科学学院国家民委分析化学重点实验室

出处《化学与生物工程》 CAS 2012年第7期51-55,共5页 Chemistry & Bioengineering

关键词磁性纳米微球双甘膦吸附 DNA magnetic nanospheres PMIDA adsorption DNA

分类号 TQ138.11 [化学工程—无机化工]

引文网络
相关文献

参考文献11

1Sambrook J, Russel D W. Molecular Cloning(3rd edition)[ M]. Beijing: Science Press, 2002 : 26-61.
2Xie X, Zhang X. Preparation and application of surface-coated superparamagnetie nanobeads in the isolation of DNA[J]. J Magn Magn Mater, 2004, 277(1-2) : 16-23.
3Spanovd Alena, Rittich Bohuslav, Benes Milan J, et al. Ferrite supports for isolation of DNA from complex samples and polymerase chain reaction amplification[J]. J Chromatogr A, 2005, 1080 (1) : 93-98.
4Mophpatra S, Pramanik N, Ghosh S K, et al. Synthesis and characterization of ultrafine poly(vinylalcohol phosphate)coated magnetite nanoparticles[J]. Nanosci Nanotechnol, 2006,6 (3) : 823-828.
5Mophpatra S, Pramanik P. Synthesis and stability of functionalized iron oxide nanoparticles using organophosphorus coupling agent[J]. Colloids Surf A, 2009,339(1-3) :35-42.
6Roberts D,Zhu W L, FromMen C M. et al. Synthesis of gadolinium oxide magnetoliposomes for magnetic resonance imagine[J]. J Appl Phys, 2000,87 (9): 6208-6210.
7Sahu Sumanta Kumar, Chakrabarty Arindam, Bhattacharya I)-psikha, et al. Single step surface modification of highly stable magnetic nanoparticles for purification of His-tag proteins[J]. J Nanopart Res,2011,13(6) :2475-2484.
8苗兰冬.双甘膦中总磷测定的消解方法探讨[J].四川化工,2010,13(5):37-39. 被引量：3
9Werner Stober,Arthur Fink, Bohn E. Controlled growth of monodisperse silica spheres in the micron size range[J]. J Coil Interf Sci,1968,26(1) :62-69.
10Harvey S C. DNA structural dynamics: Longitudinal breathing as a possible mechanism for B-Z transition[J]. Nucleic Acids Res, 1983,11(14) :4867-4877.