在电解液1 mol/L LiPF6/EC+DMC中加入碳酸钠(Na2CO3),通过SEM、循环伏安和电化学阻抗谱分析,研究了Na2CO3对石墨电极的影响。添加饱和Na2CO3,可促进在石墨电极表面形成更稳定的固体电解质相界面(SEI)膜,抑制循环过程中电解液的进一步还原分解,增进Li+嵌脱过程的可逆性,改善石墨电极的电化学性能。
Effects of sodium carbonate（ Na2CO3） on graphite electrode were studied through SEM, cyclic voltammetry and elec- trochemical impedance spectroscopy analyses by adding Na2CO3 into electrolyte 1 mol/L LiPF6/EC ＋ DMC. Adding saturated N2CO3 could help to form a more stable solid electrolyte interphase （SEI） film, suppress the decomposition of electrolyte, enhance the reversibility of Li＋ insertion and extraction process, improving the electrochemical performance of graphite electrode.