摘要
An 88 nm gate-length In0.53Ga0.47As/In0.52Alo.48As InP-based high electron mobility transistor （HEMT） was successfully fabricated with a gate width of 2× 50 μm and source-drain space of 2.4μm. The T-gate was defined by electron beam lithography in a trilayer of PMMA/A1/UVIII. The exposure dose and the development time were optimized, and followed by an appropriate residual resist removal process. These devices also demonstrated excellent DC and RF characteristics： the extrinsic maximum transconductance, the full channel cur- rent, the threshold voltage, the current gain cutoff frequency and the maximum oscillation frequency of the HEMTs were 765 mS/mm, 591 mA/mm, -0.5 V, 150 GHz and 201 GHz, respectively. The HEMTs are promising for use in millimeter-wave integrated circuits.
An 88 nm gate-length In0.53Ga0.47As/In0.52Alo.48As InP-based high electron mobility transistor （HEMT） was successfully fabricated with a gate width of 2× 50 μm and source-drain space of 2.4μm. The T-gate was defined by electron beam lithography in a trilayer of PMMA/A1/UVIII. The exposure dose and the development time were optimized, and followed by an appropriate residual resist removal process. These devices also demonstrated excellent DC and RF characteristics： the extrinsic maximum transconductance, the full channel cur- rent, the threshold voltage, the current gain cutoff frequency and the maximum oscillation frequency of the HEMTs were 765 mS/mm, 591 mA/mm, -0.5 V, 150 GHz and 201 GHz, respectively. The HEMTs are promising for use in millimeter-wave integrated circuits.