摘要
用水泥提取液模拟混凝土孔隙液,用自腐蚀电位、动电位极化和电化学阻抗技术,研究单掺粉煤灰或矿粉、复掺粉煤灰和矿粉对混凝土中钢筋氯盐腐蚀行为的影响.结果表明,粉煤灰和矿粉均能有效降低钢筋受氯离子腐蚀的风险,减小腐蚀速率,并能不同程度地提高钢筋腐蚀的临界氯离子浓度.抑制氯离子腐蚀能力由强到弱依次为:矿粉>矿粉+粉煤灰>粉煤灰>水泥.且随氯离子浓度的增大,矿粉和粉煤灰的阻锈效率会有不同程度的下降.用矿粉和粉煤灰按适当比例复掺的方法来对抗氯离子腐蚀不仅经济,而且有不错的阻锈效果.
By means of free corrosion potential measurement, potentiodynamic and electrochemical impedance spectroscopy etc, the effect of fly ash and slag on corrosion behavior of reinforcing rebar was investigated in solution of cement extract with contaminant of chlorides, which was adopted to simulate the known concrete pore solution in reinforcements. The results show that fly ash and slag can effectively reduce the risk of chloride induced corrosion and the corrosion rate of reinforcing steel rebar. Besides, the threshold value of chloride for corrosion is increased to some extence. The inhibition ability to chloride induced corrosion is in the order of： slag 〉 slag ＋ fly ash 〉 fly ash 〉 cement. In addition, the corrosion inhibition efficiency of slag and fly ash decreases to some extent with the increase of the chloride concentration. The admixture of fly ash and slag at a appropriate proportion is excellent corrosion inhibitor for chloride induced corrosion to steel rebar in terms of cost and effectiveness.
出处
《腐蚀科学与防护技术》
CAS
CSCD
北大核心
2012年第3期218-222,共5页
Corrosion Science and Protection Technology
基金
国家自然科学基金项目(50978085)
江苏省“六大人才高峰”项目(2009218)
中国博士后科学基金项目(20100481082)
江苏省博士后科研资助计划项目(1002019B)
中央高校基本科研业务费项目(2009B15214)资助
关键词
矿物掺合料
模拟孔隙液
自腐蚀电位
动电位极化
电化学阻抗谱
mineral admixture, simulated concrete pore solution, corrosion potential, potentiody- namic polarization, electrochemical impedance spectroscopy