摘要
采用4因子3水平正交实验方案,用含十二烷基硫酸钠(K12)和碳酸钠的溶液对腈纶针织物进行了抗起毛起球整理,并对织物试样进行了物理机械性能测试。对所得数据进行分析发现,温度对织物起毛起球性能的影响最大。最佳工艺为温度60℃,时间20 min,K12用量2 g/L,碳酸钠用量2 g/L。经该工艺条件处理后,腈纶针织物的抗起毛起球性能明显提高。
An orthogonal experimental design with four factors and three levels by using the solution containing sodium dodeeyl sulfate and sodium carbonate is employed for treating acrylic knitted fabric to improve its anti-pilling performance with fabric＇ s changes on physical properties tested and the obtained data analysed. The result shows that the treatment temperature mostly affects the anti-pilling performance of the fabric. The optimal treatment condition is under temperature at 60℃ for 20min with the solution containing K12 2g/L, and sodium carbonate 2g/L.