摘要
添加Y合金化、配制AlCrYZr合金 ,采用金相、X射线衍射、透射电镜、扫描电镜、力学拉伸实验等研究手段 ,研究了快速凝固AlCrYZr合金粉末挤压成形工艺以及其对组织性能的影响。结果表明 ,实验合金中主要第二相为Al2 0 Cr2 Y(立方 ,a =1 .44nm)和Al3Zr ;挤压成形时提高挤压比 ,降低挤压温度 ,有利于改善粉体结合状况 ,得到Ll2 Al3Zr质点 ,同时细化Al2 0Cr2 Y质点 ,使合金获得动态回复组织 ,从而使合金具有良好的低温、高温强度和塑性。
An AlCrYZr aluminum alloy was made up by adding alloy element yttrium. By using of optical microscopy, x-ray diffration, transsion electron microscopy, scanning eletron microscopy and tensile test, extrusion forming process of rapidly solidified powder of AlCrYZr aluminum alloy was studied and its effect on microstrutures and mechanical properties of the alloys were investigated. The results show, the main second phase of the testing alloy are Al 20 Cr 2Y(Cubic, a= 1.44 nm)and DO 23 Al 3Zr,and to increase extrusion ratio and lower extrusion temperature during extrusion forming is benificial for improving binding state of powder, obtaining Ll 2Al 3Zr precipitated particle and making Al 20 Cr 2Y particle fine and then getting dynamic recovery microstructure in the aluminum matrix, therefore, the alloy prepared by using a suitable consolidation roue has good strength and plasticity at room temperature and evelated temperature.
出处
《粉末冶金技术》
CAS
CSCD
北大核心
2000年第1期23-27,共5页
Powder Metallurgy Technology
基金
国家高技术"86 3"计划新材料领域资助项目
国家"九五"攻关项目
关键词
铝合金
快速凝固
挤压
强度
塑性
aluminum alloy
rapid solidification
extrusion