摘要
Stripping dispersion hollow fiber liquid membrane system（SDHFLM） containing feed phase adding acetate buffer solution and dispersion solution with HNO_3 solution as the stripping solution and membrane solution of 2-ethyl hexyl phosphoric acid-mono-2-ethylhexyl ester（PC-88A） dissolved in kerosene,has been studied for the extraction of Sm^（3＋）.Many factors including pH value, volume ratio of membrane solution to stripping solution（OAV） and carrier concentration on Sm^（3＋） extraction were investigated. Experimental results indicate that the optimum extraction conditions of Sm^（3＋） were obtained as that PC-88A concentration was 0.120 mol/L,and OAV was 1.00 in the dispersion phase,and pH value was 4.80 in the feed phase.When initial Sm^（3＋） concentration was 1.20×10^（-4） mol/L,the extraction percentage of Sm^（3＋） was up to 92.8%in 160 min.
Stripping dispersion hollow fiber liquid membrane system（SDHFLM） containing feed phase adding acetate buffer solution and dispersion solution with HNO_3 solution as the stripping solution and membrane solution of 2-ethyl hexyl phosphoric acid-mono-2-ethylhexyl ester（PC-88A） dissolved in kerosene,has been studied for the extraction of Sm^（3＋）.Many factors including pH value, volume ratio of membrane solution to stripping solution（OAV） and carrier concentration on Sm^（3＋） extraction were investigated. Experimental results indicate that the optimum extraction conditions of Sm^（3＋） were obtained as that PC-88A concentration was 0.120 mol/L,and OAV was 1.00 in the dispersion phase,and pH value was 4.80 in the feed phase.When initial Sm^（3＋） concentration was 1.20×10^（-4） mol/L,the extraction percentage of Sm^（3＋） was up to 92.8%in 160 min.
基金
financially supported by the National Natural Science Foundation of China for Young Scientists(Nos. 51109197 and 51009126)
the Action Plan for the Development of Western China of the Chinese Academy of Sciences (No.KZCX2-XB2-13)
the Knowledge Innovation Program of the Chinese Academy of Sciences(No.KSCX2-YW-N -003)
Research Fund for Excellent Doctoral Thesis of Xi'an University of Technology(Nos.602-210805 and 602-210804)