In the present work transparent Y2O3 ceramics were made by slip casting and vacuum sintering of nanopowders with sodium poly-acrylic acid（PAA-Na） as dispersant.The rheological properties of Y2O3 nanopowder slurry were investigated using different amounts of dis-persant and solid contents.The microstructures and transmittance of the sintered ceramics were also studied by means of scanning electron microscopy（SEM） and ultra-violet visible spectrometry.The results showed that rheological behaviors of the Y2O3 nanopowder slurry were effectively promoted by sodium polyacrylic acid.Highly dispersive and stable slurries were obtained as the dispersant was added over 1.0 dwb% under the fixed conditions of pH 11 and 45 wt.% solid content.All the slip cast green bodies were sintered into highly dense ceramics after sintering at 1700 oC for 5 h in vacuum,wherein the sample added with 1.1% sodium polyacrylic acid exhibited the highest relative den-sity of 99.36% and transmission of 30% at 800 nm wavelength.
In the present work transparent Y2O3 ceramics were made by slip casting and vacuum sintering of nanopowders with sodium poly-acrylic acid（PAA-Na） as dispersant.The rheological properties of Y2O3 nanopowder slurry were investigated using different amounts of dis-persant and solid contents.The microstructures and transmittance of the sintered ceramics were also studied by means of scanning electron microscopy（SEM） and ultra-violet visible spectrometry.The results showed that rheological behaviors of the Y2O3 nanopowder slurry were effectively promoted by sodium polyacrylic acid.Highly dispersive and stable slurries were obtained as the dispersant was added over 1.0 dwb% under the fixed conditions of pH 11 and 45 wt.% solid content.All the slip cast green bodies were sintered into highly dense ceramics after sintering at 1700 oC for 5 h in vacuum,wherein the sample added with 1.1% sodium polyacrylic acid exhibited the highest relative den-sity of 99.36% and transmission of 30% at 800 nm wavelength.
作者
HUO Di
ZHENG Yanchun
SUN Xudong
LI xiaodong
LIU Shaohong
霍地;郑艳春;孙旭东;李晓东;刘绍宏(Key Laboratory for Anisotropy and Texture of Materials(Ministry of Education),Northeastern University,Shenyang 110004,China;Liaoning Upcera Biological Materials Co.,Ltd.,Shenyang 110034,China)
基金
Project supported by Liaoning Provincial Natural Science Foundation (a20062019)
National Natural Science Foundation of China (50990303,51072030)