摘要
对Al-Mn合金的显微组织、力学性能以及在不同热处理状态下的力学性能进行了研究。研究结果表明:Al-Mn合金的显微组织为a固溶体基体上分布着AlMn6和Al11Mn4金属间化合物,随着锰含量的增加,析出金属化合物数量增加,晶粒变粗;合金在Mn含量为0.90wt%～2.15wt%的范围内,强度随含Mn量的增加而增加;当含Mn量大于2.15%时,强度随含Mn量的增加而降低。Al-Mn合金的硬度随含锰量的增加而增加,塑性韧性随含Mn量的增加而下降;Al-Mn合金不能通过热处理进行强化。
Microstructure and mechanics properties of the Al-Mn alloy under different thermal treatment were researched.Research results show that the microstructure of alloy is AlMn6 和Al11Mn4 distributing on a solid basement.With increasing content of Mn,the precipitations increase,and grains become bulky.When the content of Mn is within the range of 0.90%～2.15%,the strength of alloy increases along the content of Mn increaseing.After the content above 2.15%,with the increase of Mn content,the strength decreases.The Al-Mn alloy hardness increases,and its plasticity and toughness decrease,with the increase of Mn content.Al-Mn alloy cannot be intensified by thermal treatment.
出处
《热加工工艺》
CSCD
北大核心
2012年第1期5-7,11,共4页
Hot Working Technology
基金
国家自然科学基金项目<高矿化度水质下三氧二铝颗粒增强铝锰合金复合材料的冲蚀腐蚀机制研究>资助项目(50861008)
关键词
铝锰合金
组织
性能
Al-Mn alloy
microstructure
property