硅源对莫来石结合刚玉耐火材料性能的影响 被引量:2

Effects of different SiO_2 resources on properties of mullite bonded corundum refractory
在线阅读 下载PDF
导出
摘要 以板状刚玉为骨料,莫来石为结合相,并以高岭土和无定型SiO2微粉作为合成莫来石的硅源,采用反应烧结工艺制备莫来石结合刚玉耐火材料,旨在降低莫来石的烧结成本及获得理想的显微结构.研究表明:以高岭土为硅源,莫来石生成量低于理论量,但生成温度较低,1550℃前已完成莫来石化反应,显微结构较均匀,烧结程度较好,莫来石呈长柱状;以SiO2微粉为硅源,莫来石量随温度提高连续增多,至1650℃接近理论生成量,莫来石呈粒状并倾向于偏聚,显微结构整体致密但局部疏松;后者强度,尤其高温强度显著高于前者,但抗热震性低于前者. Tabular corundum was used as the aggregates,and two kinds of cheap and highly reactive raw materials including clay and SiO2 powder were used as the SiO2 resources for synthesis mullite matrix,so that the mullite-corundum composite refractory was prepared by reactive sintering to reduce the cost of mullite sintering and to obtain ideal microstructures.For the sintered sample using clay as the SiO2-containing raw material,mullite synthesized amount is lower than the academic amount,but the mullite synthesized temperature is lower,and the mullite synthesized reaction is finished before 1550 ℃.The microstructure is more homogeneous with rod-shaped mullite grains.The sintering degree is better.For the sintered samples with SiO2 powder as the raw material of matrix,the amount of synthesized mullite is increased continuously with the increasing of sintering temperature and reaches to a complete mullitization at 1650 ℃.The granular mullite grains in the matrix tend to aggregate.The microstructure is dense but loose in local regions.The latter has higher strength but lower thermal shock resistance than the former.
出处 《材料科学与工艺》 EI CAS CSCD 北大核心 2011年第5期35-39,共5页 Materials Science and Technology
基金 西安建筑科技大学人才科技基金项目(RC1039)
关键词 复相耐火材料 高岭土 硅微粉 莫来石 性能 composite refractory clay SiO2 powder mullite properties
  • 相关文献

参考文献15

  • 1MONTES O B, NIETO M I, MORENO R. Mullite compacts obtained by colloidal filtration of alumina powders dispersed in colloidal silica suspensions[J]. Ceram Int, 2007, 33 (3) : 327 - 332.
  • 2SCHNEIDER I-I, SCHREUER J, HILDMANN B. Structure and properties of mullite A review [ J]. J Eur Ceram Soe, 2008, 28:329 -344.
  • 3GANESH I, FERREIRA J M F. Influence of raw material type and of the overall phase formation and sintered aggregates [ J ]. Ceram Int, 2015. chemical composition on microstrueture of mullite 2009, 35 (5) : 2007 -.
  • 4SACKS M D, BOZKURT M, SCHEIFFELE G W. Fabrication of mullite-matrix composites by transient viscous sintering of composite powders[J]. J Am Ceram Soc, 1991, 74(10) : 2428 -2437.
  • 5KARA F, LITTLE J A. Sintering behaviour of precursor mullite powders and resultant microstructures [ J]. J Eur Ceram Soc, 1996, 16:627-635.
  • 6VIEIRA S C, RAMOS A S, VIEIRA M T. Mullitization kinetics from silica-and alumina-rich wastes [ J]. Ceram Int, 2007, 33 (1) : 59 - 66.
  • 7SCHNEIDER H, OKADA K, PASK J A. Mullite and mul- lite ceramics [M]. England:John Wiley & Sons, 1994.
  • 8SOUTO A, GUITION F. Purification of mullite by re- duction and volatilization of impurities [ J ]. J Am Ceram Soc, 1999, 82(10) : 266 -2664.
  • 9CHEN C Y, LAU G S, TUAN W H. Microstructural evolution of mullite during the sintering of kaolin powder compacts [ J] Ceram Int, 2000, 26:715-720.
  • 10TEZUKA N, LOW I M, DAVIES I J, et al. In situ neutron diffraction investigation on the phase transfor- mation sequence of kaolinite and halloysite to mullite [J]. PhysicaB, 2006, 385-386(15): 555-557.

同被引文献44

引证文献2

二级引证文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部