用Kevlar和Nomex丝束与金属纤维丝束进行混编、加捻成纱,织成平纹和斜纹织物,然后进行染色与抗光老化同浴整理,研制出综合性能优良的抗电磁辐射-抗光老化芳纶织物。结果表明,此功能面料克重小于205 g/m2;强度高于900N;经人工紫外辐射加速老化后,其强度保持率高达80%-85%;阴燃时间短于5s;电磁屏蔽效能在宽的频率范围内高达40dB。可见,由该技术可制备出轻质、高强、阻燃、抗电磁辐射、且抗光老化综合性能良好的多功能织物。
In our work,commercial Kevlar / Nomex products and metal fiber bundles were mixed and twisted into yarn to weave plain fabrics and twill fabrics,respectively. Moreover,the two kinds of fabrics were finished by single-bath using dyeing and anti-photoaging agents to prepare high performance anti-electromagnetic radiation / anti-photoaging aramid fabrics.The results show that its weight is less than 205 g/m2,broken strength is higher than 900N,strength retention（after artificially accelerated ageing testing） is up to 80%～85%,smoldering time is less than 5s,and electromagnetic shielding effectiveness is up to 40dB.It is thus clear that low-density,high strength,flame retardancy,anti-electromagnetic radiation,and anti-photoaging multi-functional aramid fabrics were developed using our technology.Besides,this technology is simple operation and applicable to industrial production.
出处
《高分子材料科学与工程》
EI
CAS
CSCD
北大核心
2011年第9期146-149,共4页
Polymer Materials Science & Engineering
基金
上海市重点学科建设项目资助(s30107)
上海大学创新基金
国防科工委项目(JPPT-115-919)
关键词
抗电磁辐射
抗光老化
芳纶织物
anti-electromagnetic radiation
anti-photoaging
aramid fabric