摘要
采用熔体快淬法及真空退火工艺制备了不同淬速的Nd8.5Fe77.7Nb2Co5Ga0.6B6.2粘结磁体,研究了不同淬速下磁体的磁性能及温度系数。结果表明,适当的快淬速度有利于合金退火后的晶粒细化,有效地改善了退火后软、硬磁相间的交换耦合作用。快淬速度对磁体的温度系数有显著的影响,矫顽力温度系数β随着淬速的增加而逐渐降低;随着淬速的增加,剩磁温度系数α先降低后升高,这可能与合金中软、硬磁相间的交换耦合作用的变化有密切的关系。
Nanocomposite Nd8.5Fe77.7Nb2Co5Ga0.6B6.2 bonded magnets were prepared by melt-spun and vacuum annealing processes.The dependence on the melt-spun speed of magnetic properties and temperature coefficients of the magnets was investigated.The results show that a proper melt-spun speed is beneficial to the grain refinement and the exchange coupling effect between the Nd2Fe14B and α-Fe phases of the alloys annealed is greatly improved.It is also shown that the temperature coefficients are significantly influenced by the melt-spun speed.With the increase of the melt-spun speed,the temperature coefficient β of coercivity is continuously decreased.The temperature coefficient α of remanence is decreased first and then increased with the increase of the melt-spun speed.It might be closely related to the exchange coupling effect between the Nd2Fe14B and α-Fe phases.
出处
《稀有金属材料与工程》
SCIE
EI
CAS
CSCD
北大核心
2011年第8期1450-1453,共4页
Rare Metal Materials and Engineering
基金
国家自然科学基金(50671059)
上海市重点学科建设项目(S30107)
关键词
纳米晶复合永磁材料
温度系数
快淬速度
交换耦合作用
nanocomposite magnets
temperature coefficient
melt-spun speeds
exchange coupling effect