摘要
利用离子液体AmimCl溶解结合超临界CO2干燥的方法制备了纤维素气凝胶材料.研究了不同初始浓度的纤维素溶液及其在不同凝固浴中制备的纤维素凝胶的流变行为,进一步考察了纤维素溶液浓度和凝固浴种类对纤维素气凝胶材料结构的影响.结果表明,随着初始纤维素溶液浓度的增大,气凝胶的孔结构逐渐致密,比表面积随之减小;凝固浴的组成对纤维素气凝胶的结构也有较大影响.采用适当的制备条件,可以制备出高比表面积的纤维素气凝胶材料.对纤维素气凝胶的热性能进行了表征,结果表明所得到的气凝胶材料具有较好的热稳定性和较高的炭残余含量.
Cellulose aerogel materials were prepared by combining dissolving cellulose in an ionic liquid,1-allyl-3methylimidazolium chloride （AmimCl）,and drying in supercritical CO 2.The rheological properties of the cellulose solutions of different concentrations and their gels regenerated in different coagulation baths were studied.The porous structure and morphology of cellulose aerogels were found to be affected by cellulose concentration and nature of the coagulation bath.With increasing initial cellulose concentration,the porous structure of cellulose aerogels became more dense and uniform,leading to the gradual decrease of the specific surface area.Further,it was also observed that,both viscosity and the polarity of coagulation bath affected the structure of cellulose aerogels.High specific surface area cellulose aerogel materials could be prepared by controlling the experimental conditions.The obtained cellulose aerogels had relatively high char yield at elevated temperature,which makes them potential precursors for fabrication of novel mesoporous carbon materials.
出处
《中国科学：化学》
CAS
CSCD
北大核心
2011年第8期1331-1337,共7页
SCIENTIA SINICA Chimica
基金
国家自然基金(50821062
50873111)
国家高技术研究发展计划(2009AA033601)
国家重点基础研究发展计划(2010CB934705)
中国科学院方向性创新项目(KJCX2-YW-H30-03)资助