摘要
本文通过对机械球磨方法制备的FeSiAl非晶粉末进行Mssbauer谱分析,研究非晶的形成过程。经12小时球磨后,基体组织中非晶含量高达80％以上,将其非晶粉末压制退火后仍为原来的DO_3结构。
The forming process of amorphous state of FeSiAl amorphous powder prepared by mechanical ball milling has been studied by means of Mossbauer spectrometer. The content of amorphous state in the matrix was over 80% after ball milling for 12 hours, the original DO3 structure was still maintained after pressing and annealing of the smorphous powder.