摘要
对湘钢烧结配加印度矿进行了试验研究，结果表明：试验所用的印度果阿矿，因其粒度细，ＳｉＯ２含量低，烧损大，与澳大利亚矿相比，在相同条件下，烧结速度较低，烧结矿强度有所下降。不过，适当调整工艺参数，仍能保持与澳矿相近的烧结速度和烧结矿强度。
The sintering test of proportioning of Indian iron ore in Xian Tan I&S Co. was conducted.The result shows,as the Goa iron ore has finer partical size ,lower SiO2 content,larger loss on ignition, sothat the sintering speed was lower and the strength of sinter was also decreased as compared with Austrlian iron ore . Through process parameter adjusting,the similar sintering speed and sinter strength can be obtaind,but the metallurgical properties were decreased.
出处
《烧结球团》
北大核心
1999年第4期31-34,共4页
Sintering and Pelletizing