Tempering Behavior of 4.5Cr-2W-0.25V Steel 被引量:5

Tempering Behavior of 4.5Cr-2W-0.25V Steel
原文传递
导出
摘要 The tempering behavior of a Cr-W-V steel was investigated in this research. This new alloy with the com- position of Fe-4.5Cr-2W-0. 25V-0. 1C was austenitized at 1 000 ℃ for 30 rain and tempered at 600 and 700 ℃ for dif- ferent time up to 100 h. An OM analysis of the microstructure of air cooled and water quenched specimens before tempering showed that although under both conditions fully martensitic matrix formed, finer structure had formed in the water quenched specimens. The XRD and TEM results showed that the most stable carbides formed during tempering of the steel were M23C6 and M7C3, respectively. Other carbides such as M3C and M2C, formed in the first stages of tempering, and stable MC were also observed. The results showed that when the tempering time, tempera- ture and cooling rate were increased, mass percent of extracted precipitates was increased. In addition, the formation rate of the stable carbides such as M23 Cs and dissolution rate of the metastable carbides such as M3C and M2C were increased. The tempering behavior of a Cr-W-V steel was investigated in this research. This new alloy with the com- position of Fe-4.5Cr-2W-0. 25V-0. 1C was austenitized at 1 000 ℃ for 30 rain and tempered at 600 and 700 ℃ for dif- ferent time up to 100 h. An OM analysis of the microstructure of air cooled and water quenched specimens before tempering showed that although under both conditions fully martensitic matrix formed, finer structure had formed in the water quenched specimens. The XRD and TEM results showed that the most stable carbides formed during tempering of the steel were M23C6 and M7C3, respectively. Other carbides such as M3C and M2C, formed in the first stages of tempering, and stable MC were also observed. The results showed that when the tempering time, tempera- ture and cooling rate were increased, mass percent of extracted precipitates was increased. In addition, the formation rate of the stable carbides such as M23 Cs and dissolution rate of the metastable carbides such as M3C and M2C were increased.
出处 《Journal of Iron and Steel Research International》 SCIE EI CAS CSCD 2010年第10期57-62,共6页
关键词 Cr-W-V steel CARBIDE TEMPERING TEM XRD Cr-W-V steel carbide tempering TEM XRD
  • 相关文献

参考文献21

  • 1Carlan Y de, Murugananth M, Sourmail T, et al. Design of New Fe-9CrWV Reduced Activation Martensitic Steels for Creep Properties at 650 ℃ [J]. J Nuct Mater, 2004, 329-333 238.
  • 2Zinkle S J. Advanced Materials for Fusion Technology [J]. Fusion Eng Des, 2005, 74: 31.
  • 3Jones R H, Heinisch H L, McCarthy K A. Low Activation Materials [J].J Nucl Mater, 1999, 271-272: 518.
  • 4Ioltukhovskiy A G, Blokhin A I, Budylkin N I, et al. Material Science and Manufacturing of Heat-Resistant Reduced-Activation Ferritie-Martensitic Steels for Fusion[J]. J Nucl Mater, 2000, 283-287:652.
  • 5Chen Z, Shah Z W, Wu N Q, et al. Fine Carbide-Strengthened 3Cr-3WVTa Bainitie Steel [J]. Metall Mater Trans A, 2004, 35(4): 1281.
  • 6Robson J D, Bhadeshia H K D H. Modelling Precipitation Sequences in Power Plant Steels Part 2--Application of Kinetic Theory [J]. Mater Sci Tech, 1997, 13: 640.
  • 7Gustafson P. A Thermodynamic Evaluation of the C-Cr-Fe-W System[J]. Metall Mater Trans A, 1988, 19(10) : 2547.
  • 8Kim S H, Ryu W S, Kuk H H. Microstructure and Mechanical Properties of Cr-Mo Steels for Nuclear Industry Applications[J]. J Korean Nucl Soc, 1999, 31(6):561.
  • 9Fujita N, Bhadeshia H K D H. Modelling Simultaneous Alloy Carbide Sequence in Power Plant Steels [J]. ISIJ Int, 2002, 42 (7) : 760.
  • 10Klueh R L. Heat Treatment Behavior and Tensile Properties of Cr-W Steels[J].Metall Trans A, 1989, 20: 463.

同被引文献48

引证文献5

二级引证文献23

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部