Carbon fibre reinforced carbon and silicon carbide dual matrix composites（C/C-SiC） were fabricated by the warm compacted-in situ reaction.The microstructure,mechanical properties,tribological properties,and wear mechanism of C/C-SiC composites at different brake speeds were investigated.The results indicate that the composites are composed of 58wt%C,37wt%SiC,and 5wt%Si.The density and open porosity are 2.0 g.cm^（-3） and 10%,respectively.The C/C-SiC brake composites exhibit good mechanical properties.The flexural strength can reach up to 160 MPa,and the impact strength can reach 2.5 kJ.m^（-2）.The C/C-SiC brake composites show excellent tribological performances.The friction coefficient is between 0.57 and 0.67 at the brake speeds from 8 to 24 m·s^（-1）.The brake is stable,and the wear rate is less than 2.02×10^（-6） cm^3·J^（-1）.These results show that the C/C-SiC brake composites are the promising candidates for advanced brake and clutch systems.
Carbon fibre reinforced carbon and silicon carbide dual matrix composites（C/C-SiC） were fabricated by the warm compacted-in situ reaction.The microstructure,mechanical properties,tribological properties,and wear mechanism of C/C-SiC composites at different brake speeds were investigated.The results indicate that the composites are composed of 58wt%C,37wt%SiC,and 5wt%Si.The density and open porosity are 2.0 g.cm^（-3） and 10%,respectively.The C/C-SiC brake composites exhibit good mechanical properties.The flexural strength can reach up to 160 MPa,and the impact strength can reach 2.5 kJ.m^（-2）.The C/C-SiC brake composites show excellent tribological performances.The friction coefficient is between 0.57 and 0.67 at the brake speeds from 8 to 24 m·s^（-1）.The brake is stable,and the wear rate is less than 2.02×10^（-6） cm^3·J^（-1）.These results show that the C/C-SiC brake composites are the promising candidates for advanced brake and clutch systems.
基金
supported by the National High-Tech Research and Development Program of China(No.2006AA03Z560)
the Graduate Degree Thesis Innovation Foundation of Central South University(No.2008yb019)