摘要
以过硫酸钾为引发剂,甘油溶液为交联剂,引发甘薯淀粉与丙烯酸接枝共聚反应。对影响反应的主要因素如丙烯酸中和度、引发剂的量、交联剂的量、体系用水量、淀粉糊化时间进行了研究。结果表明,淀粉接枝丙烯酸共聚高吸水树脂的最佳工艺条件为:丙烯酸中和度为70%,引发剂的量为60 mg,交联剂量为0.25 mL,体系用水量为40 mL,淀粉糊化时间为20 min。按此条件制得的树脂的吸水率为768
Graft polymerization of acrylic acid onto sweet starch using potassium per sulfate-sodium bisulfate as initiators,glycerol as crosslinking agent,effect of the degree of neutralization of monomer,the concentration of initiators and crosslinking agent,the volume of water,the time of starch gelatinization on reaction were studied.The result showed that the grafting percentage is higher when the neutral degrade is 70%,concentrations of initiator and crosslinking agent are at 60 mg and 0.25 mL,the volume of water is 40 mL,the time of starch gelatinization is 20 min.Under the condition,the water absorption rate of resin is 768 g/g.