The microstructure and magnetic properties of Co/Cr bilayer films were examined before and after postdeposition annealing by using transmission electron microscopy （TEM）, X-ray diffraction （XRD） technique and vibrating sample magnetometer （VSM）. A model of grain boundary （GB） Cr-rich phase growth involving GB diffusion derived from the Cr underlayer was proposed to elucidate the kinetics of the paramagnetic Cr-rich phase growth along Co GBs within the Co layer. The correlation of the GB Cr-rich phase formation with the magnetic Co grain isolation and accordingly, improvement of magnetic properties was experimentally investigated and discussed in detail. Our analysis results are well consistent with previous micromagnetic simulations on the improvement of magnetic properties by the magnetic grain isolation. The results provide some insights into the processing-structure-property relationships of the Co/Cr bilayer films, and thus suggest that the magnetic grain isolation be feasible not only in longitudinal recording media, but also be effective in tuning the exchange coupling of magnetic grains in perpendicular recording media via the GB diffusion from underlayer and/or overlayer.
The microstructure and magnetic properties of Co/Cr bilayer films were examined before and after postdeposition annealing by using transmission electron microscopy （TEM）, X-ray diffraction （XRD） technique and vibrating sample magnetometer （VSM）. A model of grain boundary （GB） Cr-rich phase growth involving GB diffusion derived from the Cr underlayer was proposed to elucidate the kinetics of the paramagnetic Cr-rich phase growth along Co GBs within the Co layer. The correlation of the GB Cr-rich phase formation with the magnetic Co grain isolation and accordingly, improvement of magnetic properties was experimentally investigated and discussed in detail. Our analysis results are well consistent with previous micromagnetic simulations on the improvement of magnetic properties by the magnetic grain isolation. The results provide some insights into the processing-structure-property relationships of the Co/Cr bilayer films, and thus suggest that the magnetic grain isolation be feasible not only in longitudinal recording media, but also be effective in tuning the exchange coupling of magnetic grains in perpendicular recording media via the GB diffusion from underlayer and/or overlayer.
基金
supported by the National Natural Sci-ence Foundation of China (No 50671020)
the Chinese Ministry of Education (Nos 108039 and IRT0713)