摘要
The yellow indium oxide nanoparticles were prepared by sintering the white deposition at 500 ℃. The crystalline indium chloride and ammonia were used as the starting material. The results show that, by analyzing the particles through X-ray diffraction and TEM, the particles are very small, spherical, and the particle size is about 40 nm. The direct-heat components made from indium oxide in Cl2 and NO2 was tested respectively, the component is far more sensitive to NO2 than to Cl2 at low heating temperature, and the status is reversed at high heating temperature..
The yellow indium oxide nanoparticles were prepared by sintering the white deposition at 500℃. The crystalline indium chloride and ammonia were used as the starting material. The results show that, by analyzing the particles through X-ray diffraction and TEM, the particles are very small, spherical, and the particle size is about 40 nm. The direct-heat components made from indium oxide in Cl2 and NO2 was tested respectively, the component is far more sensitive to NO2 than to Cl2 at low heating temperature, and the status is reversed at high heating temperature.
出处
《中国有色金属学会会刊：英文版》
CSCD
2009年第B09期80-82,共3页
Transactions of Nonferrous Metals Society of China
基金
Project(2007AA03Z325) supported by the National High Technology Research and Development Program of China
Project(T0750004) supported by the Natural Science Foundation of Fujian Province,China