采用XRD、IR和原子吸收光谱等手段对微波固相法制备的ZnCl2／Y催化剂进行了表征·微波辐射促进了ZnCl2在分子筛表面分散和固态离子交换，分散的ZnCl2可与分子筛表面氧原子发生较强的配住键合作用．当ZnCl2的负载量达到37．5％时，ZnCl2仍可完全分散于NaY分子筛表面，此时的固态离子交换度为84％．随着分子筛表面酸菌和区强度的增加，ZnCl2与分子筛的固态离子交换量减少．
ZnCl2/Y catalysts prepared by solid-state reaction of anhydrous ZnCl2 and Y zeolites under microwave irradiation were characterized by XRD, IR and AAS. ZnCl2 was intercalated in Y zeolites and dispersed on the surface of Y zeolite, part of ZnCl2 dispersed could result in solid-state ion exchange with Y. The amount of dispersion and solid-state ion exchange were related to ZnCl2 loading and the surface acid property of the zeolite. When ZnCl2 loading was 37.5% (mass fraction) in NaY zeolite, ZnCl2 was still completely dispersed on the surf are of zeolite and the degree of solid- state ion exchallg was 84%. The appearance of new balld at 890 cm-l in the framework IR spectra of ZnCl2/NaY sample was due to the dispersed ZnCl2 coordinating strongly with oxygen of NaY surface. With the increasing of the number of arid centers and the acid strength of the surface of Y zeolite the amount of solid-state ion exchange decreased.
出处
《物理化学学报》
SCIE
CAS
CSCD
北大核心
1998年第5期448-452,共5页
Acta Physico-Chimica Sinica
基金
国家自然科学基金!29572042
关键词
微波辐射
锌
氯化锌
Y分子筛
固相反应
催化剂
Microwave irradiation, ZnCl2, Y zeolite, Solide-state reaction, Catalyst