Heterogeneous composite BaZr0.9Y0.1O2.95/Na2SO4 was designed and fabricated with Y-doped BaZrO3 as matrix and Na2SO4 as dispersant by conventional powder processing to improve the total conductivity of barium zirconate. The electrical conduction of the composite was studied by electrical and electrochemical methods. Microstructure of the heterogeneous composite was examined by SEM. The experimewtal results show that the protonic conductivity of Y-doped BaZrO3 is greatly improved upon incorporating Na2SO4 in the material. Microstructure observation indicates that a multiphase structure with Na2SO4 disperses at the grain boundaries of BaZr0.1Y0.9O2.95. Electromotive force （EMF） measurements under fuel cell conditions reveal that the total ionic transport number of the composite is more than 0.9 at 750 ℃.
Heterogeneous composite BaZr0.9Y0.1O2.95/Na2SO4 was designed and fabricated with Y-doped BaZrO3 as matrix and Na2SO4 as dispersant by conventional powder processing to improve the total conductivity of barium zirconate. The electrical conduction of the composite was studied by electrical and electrochemical methods. Microstructure of the heterogeneous composite was examined by SEM. The experimewtal results show that the protonic conductivity of Y-doped BaZrO3 is greatly improved upon incorporating Na2SO4 in the material. Microstructure observation indicates that a multiphase structure with Na2SO4 disperses at the grain boundaries of BaZr0.1Y0.9O2.95. Electromotive force （EMF） measurements under fuel cell conditions reveal that the total ionic transport number of the composite is more than 0.9 at 750 ℃.
基金
Funded by the National Natural Science Foundation of China(No. 50872090)