摘要
SrS∶HoF 3 thin film was prepared by double source method with electron beam evaporation. The fine structure of electroluminescence (EL) spectrum is found for the symmetry of the SrS∶HoF 3 thin film to be lower. The broadness of red peak is wider than that of ZnS∶HoF 3 thin film. Red EL emission in the SrS∶HoF 3 thin film comes from 5F 3 5I 7+ 5F 5 5I 8 transition. The intensity of blue and red emission increases obviously in the SrS∶HoF 3 EL spectrum and white EL is obtained. The EL mechanism of the SrS∶HoF 3 thin film is dominantly the energy transfer from the crystal host to luminescent centers by 4f 95d electrons.
SrS∶HoF 3 thin film was prepared by double source method with electron beam evaporation. The fine structure of electroluminescence (EL) spectrum is found for the symmetry of the SrS∶HoF 3 thin film to be lower. The broadness of red peak is wider than that of ZnS∶HoF 3 thin film. Red EL emission in the SrS∶HoF 3 thin film comes from 5F 3 5I 7+ 5F 5 5I 8 transition. The intensity of blue and red emission increases obviously in the SrS∶HoF 3 EL spectrum and white EL is obtained. The EL mechanism of the SrS∶HoF 3 thin film is dominantly the energy transfer from the crystal host to luminescent centers by 4f 95d electrons.