A micro-modeling method (MM) for the quantitative prediction of the shrinkage cavity formation in SGiron castings is proposed. The mathematical models describing the volume changes during the solidification ofspheroidal graphite cast iron are established based on the models of solidification kinetics. The shrinkage cavityformation of T-shaped SG iron castings is calculated with MM method. The calculated results are compared with theexperimental results. It is shown that the predicted size, shape and distribution of shrinkage cavity by MM methodare in good agreement with the measured results.
A micro-modeling method (MM) for the quantitative prediction of the shrinkage cavity formation in SGiron castings is proposed. The mathematical models describing the volume changes during the solidification ofspheroidal graphite cast iron are established based on the models of solidification kinetics. The shrinkage cavityformation of T-shaped SG iron castings is calculated with MM method. The calculated results are compared with theexperimental results. It is shown that the predicted size, shape and distribution of shrinkage cavity by MM methodare in good agreement with the measured results.