摘要
Critical association concentration (Ca) of ethylene-vinyl acetate copolymer (EVA) in selective solvent mixtures of 1,2-dichloroethane (DCE) (polar solvent) and cyclohexane (CYH) (non-polar solvent) was investigated. DCE is a good solvent for polyvinyl acetate (PVAc) and a poor solvent for paraffin, whereas CYH is a good solvent for the paraffin and a precipitant for PVAc. Viscosities of EVA in different compositions of the solvent mixture with and without additives were measured. Viscosity results were used to determine the C-A value of the systems. It is shown that C-A was markedly dependent on the composition of the solvent mixture and concentration and structure of the additive. Solvation and competition between hydrogen bonding and micellisation were suggested for qualitative description of the changing of C-A value observed.
Critical association concentration (Ca) of ethylene-vinyl acetate copolymer (EVA) in selective solvent mixtures of 1,2-dichloroethane (DCE) (polar solvent) and cyclohexane (CYH) (non-polar solvent) was investigated. DCE is a good solvent for polyvinyl acetate (PVAc) and a poor solvent for paraffin, whereas CYH is a good solvent for the paraffin and a precipitant for PVAc. Viscosities of EVA in different compositions of the solvent mixture with and without additives were measured. Viscosity results were used to determine the C-A value of the systems. It is shown that C-A was markedly dependent on the composition of the solvent mixture and concentration and structure of the additive. Solvation and competition between hydrogen bonding and micellisation were suggested for qualitative description of the changing of C-A value observed.
基金
The project was supported by National Natural Science Foundation of China(No.29774020).