The influence of rare earth lanthanum and cerium on impact property of structural alloy steel with extra low sulfur and oxygen was studied by impact test and microanalysis. The results showed that rare earths increased impact power of the steel when their contents were about 0.005%. Proper addition of rare earths could purify grain boundaries and decrease amount of inclusions, and reduced the possibility of crack growth along grain boundaries and through inclusions. Therefore, such steel could absorb more crack growth energy while it was impacted. However, if the content of rare earths is excessive, the grain boundary would be weakened and brittle-hard phosphates and Fe-RE intermetallic would be formed, which worsened impact toughness of steel.
The influence of rare earth lanthanum and cerium on impact property of structural alloy steel with extra low sulfur and oxygen was studied by impact test and microanalysis. The results showed that rare earths increased impact power of the steel when their contents were about 0.005%. Proper addition of rare earths could purify grain boundaries and decrease amount of inclusions, and reduced the possibility of crack growth along grain boundaries and through inclusions. Therefore, such steel could absorb more crack growth energy while it was impacted. However, if the content of rare earths is excessive, the grain boundary would be weakened and brittle-hard phosphates and Fe-RE intermetallic would be formed, which worsened impact toughness of steel.
基金
Project supported bythe Ministry of Science and Technology of China (2002BA315A-5)