摘要
The magnetic properties and the phase transformation of the partial substitution of Pr for La in LaFe11.4Si1.6 have been investigated by the means of X-ray diffraction (XRD) and vibrating sample magnetic (VSM). The results indicated that the single phase NaZn13-type cubic structure is stabilized for the compound La0.8Pr0.2Fe11.4Si1.6 and large values of the isothermal magnetic entropy change SM around the curie temperature TC～194 K in relative low magnetic fields. The maximum value︱SM︱max～37.07 J/kg·K-1 under a field of 1.5 T. Such large MCEs are attributed to the sharp change of the magnetization at the Curie temperature, the field-induced IEM transition and a strong temperature dependence of the critical field BC.
The magnetic properties and the phase transformation of the partial substitution of Pr for La in LaFe11.4Si1.6 have been investigated by the means of X-ray diffraction (XRD) and vibrating sample magnetic (VSM). The results indicated that the single phase NaZn13-type cubic structure is stabilized for the compound La0.8Pr0.2Fe11.4Si1.6 and large values of the isothermal magnetic entropy change SM around the curie temperature TC～194 K in relative low magnetic fields. The maximum value︱SM︱max～37.07 J/kg·K-1 under a field of 1.5 T. Such large MCEs are attributed to the sharp change of the magnetization at the Curie temperature, the field-induced IEM transition and a strong temperature dependence of the critical field BC.
基金
Project supported by The National Natural Science Foundation of China (50164003)