摘要
采用W／O微乳液法制备得到了Ru-Zn@SiO2催化剂，利用程序升温还原（TPR）、X射线光电子能谱（XPS）、X射线衍射（XRD）、透射电子显微镜（TEM）和N2等温吸附，脱附技术对催化剂进行了表征．结果表明，Ru以直径约2～5nm的小颗粒均匀分散在SiO2中，而Zn则以ZnO的形式高度分散在催化剂中．利用苯选择加氢制环己烯反应对其进行了评价，在研究条件下，环己烯收率最高为12．5％，此时苯转化率为45．9％．
Ru-Zn@SiO2 catalyst was prepared through W/O microemulsion method, and was characterized by temperature-programmed reduction （TPR）, X-ray photoelectron spectroscopy （XPS）, X-ray diffraction （XRD）, transmission electron microscopy （TEM） and N2 adsorption-desorptiontechnique. It can be concluded from the results that Ru particles were dispersed uniformly with diameters about 2 - 5 nm, while Zn existed as ZnO and were highly dispersed in catalyst. The selective hydrogenation of benzene was carried out over Ru-Zn@SiO2 catalyst. The cyclohexene yield was up to 12.5% when the benzene conversion was 45.9%.
出处
《河北工业大学学报》
CAS
北大核心
2009年第1期12-16,共5页
Journal of Hebei University of Technology
基金
国家自然科学基金(20636030
20706011)
天津市应用基础研究计划重点项目(07JCZDJC00100)
关键词
苯
环己烯
选择加氢
W/O微乳液
催化剂
表征
benzene
cyclohexene
selective hydrogenation
W/O microemulsion
catalyst
characterization