This paper proposes a novel super junction （S J） SiGe switching power diode which has a columnar structure of alternating p- and n- doped pillar substituting conventional n- base region and has far thinner strained SiGe p＋ layer to overcome the drawbacks of existing Si switching power diode. The SJ SiGe diode can achieve low specific on-resistance, high breakdown voltages and fast switching speed. The results indicate that the forward voltage drop of SJ SiGe diode is much lower than that of conventional Si power diode when the operating current densities do not exceed 1000 A/cm^2, which is very good for getting lower operating loss. The forward voltage drop of the Si diode is 0.66V whereas that of the SJ SiGe diode is only 0.52V voltages are 203 V for the former and 235 V for the latter. at operating current density of 10A/cm^2. The breakdown Compared with the conventional Si power diode, the reverse recovery time of SJ SiGe diode with 20 per cent Ge content is shortened by above a half and the peak reverse current is reduced by over 15%. The SJ SiGe diode can remarkably improve the characteristics of power diode by combining the merits of both SJ structure and SiGe material.
This paper proposes a novel super junction （S J） SiGe switching power diode which has a columnar structure of alternating p- and n- doped pillar substituting conventional n- base region and has far thinner strained SiGe p＋ layer to overcome the drawbacks of existing Si switching power diode. The SJ SiGe diode can achieve low specific on-resistance, high breakdown voltages and fast switching speed. The results indicate that the forward voltage drop of SJ SiGe diode is much lower than that of conventional Si power diode when the operating current densities do not exceed 1000 A/cm^2, which is very good for getting lower operating loss. The forward voltage drop of the Si diode is 0.66V whereas that of the SJ SiGe diode is only 0.52V voltages are 203 V for the former and 235 V for the latter. at operating current density of 10A/cm^2. The breakdown Compared with the conventional Si power diode, the reverse recovery time of SJ SiGe diode with 20 per cent Ge content is shortened by above a half and the peak reverse current is reduced by over 15%. The SJ SiGe diode can remarkably improve the characteristics of power diode by combining the merits of both SJ structure and SiGe material.
基金
Project supported by the National Natural Science Foundation of China (Grant No 50477012)
the Doctoral Program Foundation of Institutes of Higher Education of China (Grant No 20050700006)
the Special Scientific Research Program of the Education Bureau of Shaanxi Province,China (Grant No 05JK268)