以低品位的石灰石为原料,通过合理的配料方案,成功制备了性能优异的水泥熟料。通过岩相观察和XRD分析结果表明,实验所用生料易烧性较好,并随温度提高而明显改善,所制备的水泥熟料的主晶相是C3S和C2S。
Through proper designed plan, high quality cement clinker was obtained by using low grade limestone as raw material. Samples were investigated by petrography analysis （PA） and X-ray diffraction （XRD）. Results show that sinterability of cement raw materials was fine and was clearly improved by increasing the temperature, the main phases of the sintered cement clinker were C3S and C2S.
出处
《国外建材科技》
2008年第6期60-62,共3页
Science and Technology of Overseas Building Materials
关键词
水泥熟料
易烧性
安定性
cement clinker
sinterability
stability