CuO/γ-Al2O3 has been considered as a promising and recycling sorbent to remove sulfur dioxide from flue gas. In this study, a series of CuO/γ-Al2O3 sorbents with different CuO loadings were prepared by impregnation. The monolayer coverage of CuO supported on γ-Al2O3 determined by X-ray quantitative analysis was 0.275 g CuO/g （γ-Al2O3）. Below the monolayer coverage, CuO was found highly dispersed on γ-Al2O3. Thermogravimetric technique was used to study sulfation kinetics and sulfation recycling. It was found that the Langmuir kinetic adsorption model described well the experimental data at the rapid sulfation region of the CuO/γ-Al2O3 sorbent. The adsorption activation energy was 19.98 kJ/mol and the pre-exponential factor was 9.97× 10^-5 s^-1.Pa^-1. The CuO/γ-Al2O3 sorbent has shown good performance on regeneration, but long sulfation time might cause the deactivation of the CuO/γ-Al2O3 sorbent. It was also seen that the sulfated γ-Al2O3 support could not be reduced at 400℃.
CuO/γ-Al2O3 has been considered as a promising and recycling sorbent to remove sulfur dioxide from flue gas. In this study, a series of CuO/γ-Al2O3 sorbents with different CuO loadings were prepared by impregnation. The monolayer coverage of CuO supported on γ-Al2O3 determined by X-ray quantitative analysis was 0.275 g CuO/g （γ-Al2O3）. Below the monolayer coverage, CuO was found highly dispersed on γ-Al2O3. Thermogravimetric technique was used to study sulfation kinetics and sulfation recycling. It was found that the Langmuir kinetic adsorption model described well the experimental data at the rapid sulfation region of the CuO/γ-Al2O3 sorbent. The adsorption activation energy was 19.98 kJ/mol and the pre-exponential factor was 9.97× 10^-5 s^-1.Pa^-1. The CuO/γ-Al2O3 sorbent has shown good performance on regeneration, but long sulfation time might cause the deactivation of the CuO/γ-Al2O3 sorbent. It was also seen that the sulfated γ-Al2O3 support could not be reduced at 400℃.
基金
This work was financially supported by the National Natural Science Foundation of China (project 90210003)
the Natural Sci-ence Foundation of Beijing (No.2012010)