摘要
The 25 years＇ production and application have proved that vermicular graphite iron cylinder heads with vermicularity ≥50% satisfy the machinability and performance demand of diesel engine. The method, in which using cupola-induction furnace duplex melting and pour-over process with rare earth-ferrosilicon or rare earthsilicon compound as vermJcularizing alloy plus rare earth-magnesium-ferrosilicon as stirring alloy, is an optimal vermicularizing process for obtaining satisfied vermicularity. Using top kiss risers, enlarging kissing areas and expanding covering width and making ingates to freeze earlier are the effective measures to eliminate shrinkage, blowhole and oxide inclusions in the vermicular graphite iron cylinder heads.
The 25 years’ production and application have proved that vermicular graphite iron cylinder heads with vermicularity ≥50% satisfy the machinability and performance demand of diesel engine. The method, in which using cupola-induction furnace duplex melting and pour-over process with rare earth-ferrosilicon or rare earth-silicon compound as vermicularizing alloy plus rare earth-magnesium-ferrosilicon as stirring alloy, is an optimal vermicularizing process for obtaining satisfied vermicularity. Using top kiss risers, enlarging kissing areas and expanding covering width and making ingates to freeze earlier are the effective measures to eliminate shrinkage, blowhole and oxide inclusions in the vermicular graphite iron cylinder heads.