用'P'盐对低密度(<1.28克/厘米~3)水玻璃改性处理,可使精铸型壳残留强度σ弯稳定在(9～15)×10~5Pa范围内,初步解决了推广这一新工艺的难题.
Modification of low density (less than1.28) sodium silicate by the use of'P'salt makes retained strength of shell mold within(9-15)×100000 Pa.This work has solved the difficult Problem in generalizing the new technioue.