摘要
研究表明:加入少量的Nd元素后,合金的铸态组织得到了细化,网状的Mg17Al12相逐渐变得断续、弥散分布,同时也出现了针状的新相;随着Nd元素含量的增加Mg-6Al镁合金的抗拉强度及伸长率也都得到了明显的提高;当Nd元素含量达到1.2%时,其力学性能最好,其抗拉强度最大,为220MPa,伸长率19.8%也为最大。
The influence of neodymium additions on the mechanical properties and structure of Mg-6Al magnesium alloys has been investigated.The results showed that the structure is refined and netted Mg17Al12 phase change to be dispersal and imtermittent and acicular new phases appeared.The mechanical properties obtained obvious improvement as the increase of content of neodymium;the mechanical properties were the best with the content of neodymium 1.2%.The tensile strength of Mg-6Al-1.2Nd was the largest up to 220MPa and the elongation the largest up to 19.8%.