在180kVA实验型直流电弧炉上进行了兑入0～50％铁水冶炼工艺的试验研究。结果表明，每加入10％的铁水可使冶炼时间缩短约6．7％，电耗降低5．5％、碳含量大于0．4％，脱碳速度可超过0．1％C／min。
The test with varied hot metal charging ratio 0～50% has been carried out in a laboratory-scaleelectric arc furnace with 180 kVA transformer. The results show that with hot metal charging ratio 10% forthe testing arc furnace the power on time and consumption of electric energy reduced 6. 7% and 5. 5%respectively, and with carbon content more than 0. 4% the decarburization rate higher than 0. 1%C/min wasobtained.