摘要
本文探索了添加微量铈对Al-Li-Cu合金(2090)性能的影响,铈有延缓合金时效过程的作用;并能显著提高合金的持久寿命和抗蚀性。
In this paper, the effet of minor cerium on the properties of Al-Li-Cu alloy was investigated. The materials used in this investigation are rolled sheets of 2 or 3mm in thickness. They were solution heat treated at 540℃, then aged at 140℃, 165℃, 190℃ C(TA) or 4% stretched prior to aging(TB).The experiments show that minor cerium can retard the aging procoss and take against softening upon aging. The alloys containing cerium passess superior strengthening effect after thermomechanical treatment(TB).The test at 200℃ under a stress of 147 Mpa were performed on thermo-mcchanical treated(TB) specimens. The endurance life(rupture time) of Ce-containing alloys is longer than that of alloys free from Co. It indicates that minor Ce can effectively increase the endurance life of Al-Li-Cu alloy at 200℃ .The tensile properties were also measured before or after the specimens were soaked in 3.5% NaCl water solution for 50 hours.The results demonstrate that the corrosion resistacc of alloy is significantly improved by the addition of minor Ce.
出处
《航空学报》
EI
CAS
CSCD
北大核心
1990年第2期B076-B082,共7页
Acta Aeronautica et Astronautica Sinica
关键词
铝锂合金
铈
材料性能
时效过程
alumium-lithium alloy, aging process, thermomechanical treatment, strengthening phase, endurance life