Study on the sulfate corrosion of concrete under the action of loading

下载PDF

导出

摘要本试验研究了荷载作用下混凝土的硫酸盐腐蚀,采用在线测定方法对不同水灰比的混凝土试件进行了与干湿循环有关的SDF和MDF耐久性试验,研究荷载、干湿循环和硫酸盐侵蚀等破坏因素的单独作用及其复合作用对混凝土耐久性的影响规律;以相对动弹性模量为评价指标对多因素协同作用下的不同水灰比混凝土试件的抗硫酸盐侵蚀性能进行了表征,通过动弹性模量在硫酸盐侵蚀条件下的变化,探索更为实用的混凝土抗硫酸盐性能的评价方法,对防治混凝土硫酸盐侵蚀提出了一些对策。 The sulfate corrosion of concrete under the action of loading was researched,using the online test method to study the durability of different W/C concrete related to dry-wet cycle affected by SDF and MDF.The influence rules of the damage fact such as the action of loading, dry-wet cycle, sulfate corrosion and the combined effects to the durability of concrete are researched.Test results are figured out with respectively dynamic modulus of elasticity.This test method provides a trusty result in an effective test period.This research simulate the corrosion process of concrete structures under corrosion circumstance and loading in engineering practice and explore more useful estimate methods of concrete members, put forward some measures to prevent the sulfate corrosion.

作者黄战邢锋董必钦殷慧罗帅

机构地区深圳大学土木工程学院深圳市土木工程耐久性重点试验室

出处《混凝土》 CAS CSCD 北大核心 2008年第2期66-69,共4页 Concrete

基金国家自然科学基金资助项目(50378055) 广东省自然科学基金资助项目(04011316)

关键词硫酸盐腐蚀荷载作用干湿循环相对动弹性模量在线测量 sulfate corrosion the action of loading dry-wet cycle：respectively dynamic modulus of elasticity online test

分类号 TU528.01 [建筑科学—建筑技术科学]

引文网络
相关文献

参考文献4

1MENASHI D.Cohen and Mather.Sulfate attack on concrete-research need[J].ACl Materials Journal, 1991:62-69.
2余红发,慕儒,孙伟,缪昌文.弯曲荷载、化学腐蚀和碳化作用及其复合对混凝土抗冻性的影响[J].硅酸盐学报,2005,33(4):492-499. 被引量：42
3王爱勤,曹建国,李金玉,等.高浓度和荷载条件下混凝土硫酸盐侵蚀特性及抗侵蚀技术[C]//阎培渝,姚燕,主编.水泥基复合材料科学与技术.北京:中国建材工业出版社,1999:179-183.
4JIN Zu-quan,SUN Wei,ZHANG Yun-sheng,et al.lnteraction between sultate and chloride solution attack of concretes with and without fly ash[J].Cement and Concrete Research,2007,37(8) : 1223-1232.

二级参考文献12

1余红发,孙伟,鄢良慧,杨波.在盐湖环境中高强与高性能混凝土的抗冻性[J].硅酸盐学报,2004,32(7):842-848. 被引量：53
2SCHNEIDER U, CHEN S W. The chemomechanical effect and the mechanochemical effect on high-performance concrete subjected to stress corrosion [J]. Cem Concr Res, 1998, 28 (4): 509-522.
3SCHNEIDER U, CHEN S W. Behaviour of high-performance concrete under ammonium nitrate solution and sustained load[J]. ACI Mater J, 1999,96(1): 47-51.
4王爱勤曹建国李金玉阎培渝姚燕主编.高浓度和荷载条件下混凝土硫酸盐侵蚀特性及抗侵蚀技术[A].阎培渝,姚燕,主编.水泥基复合材料科学与技术[C].北京:中国建材工业出版社,1999.179-183.
5ZHOU Y, COHEN M D, DOLCH L W. Effect of external loads on the frost-resistant properties of mortar with and without silica fume [J]. ACI Mater J, 1994, 91(6): 595- 601.
6SUN Wei, ZHANG Yamei, YAN Handong, et al. Damage and damage resistance of high strength concrete under the action of load and freeze - thaw cycles [J]. Cem Concr Res, 1999,29(9):1 519-1 523.
7SUN Wei, MU Ru, LUO Xin, etal. Effect of chloride salt, freeze thaw cycling and externally applied load on the per formance of the concrete [J]. Cem Concr Res, 2002, 32(12): 1 859-1 864.
8MOHR P, HANSEN W, JENSEN E, etal. Transport prop erties of concrete pavements with excellent long-term in-service performance [J]. Cem Concr Res, 2000, 30 (12): 1 903-1 910.
9GUNTHER M, BIER T, HILSDORF H. Effect of curing and type of cement on the resistance of concrete to freezing in deicing salt solutions[A]. In: SCANLON J M ed. Concrete Durability[C]. ACI, SP- 100 - 49, 1987. 877-900.
10曹建国,李金玉,林莉,田军涛,关遇时,邓正刚,李芳,王爱勤.高强混凝土抗冻性的研究[J].建筑材料学报,1999,2(4):292-297. 被引量：46