摘要
分别测定了PAC电极（Pb－Ag－Ca新型阳极的简称）在MnSO4－H2SO4溶液中的阴极极化曲线（以～lgi作图）及阳极极化曲线，从图中求得：icor＝15．85μA／cm2，cor＝－0095v，Vcor＝2．95Kg／m2ann．7．09％（电极重量每年消耗的百分数）io（2）=54．70μA/cm2及io（3）=1．10μA／cm2；讨论了PAC阳极的腐蚀机理即反应（2）受反应（3）的动力学参数所控制，为EMD工业中使用该阳极提供基础性数据．
The Anodic polarization Curve(~Igi)and The Cathodic polarization Curve of PAC electrde in MnSO4 - H2SO4 Solution haven been determined by contant Potential method respctively. from FigI Calculation icor =15. 85μA/cm2. cor = - 0.095v.V cor = 2. 95Kg/m2. ann or 7. 09 % (weight ann. cor) i0 (2 ) = 54. 70μA/cm2. i0(3 ) = 1.10μa/cm2.The mechanism of Corrosion of PAC electrode haven been discussed which is The reactin (2) was Controlled by the Kinetic parameter of reaction(3). This study presents same foundational data for PAC anode used in the EMD industry.