摘要
In this paper, TitaiJum dioxide （TiO2） rutile single crystal was irradiated by infrared femtosecond laser pulses with repetition rate of 250 kHz. For a P-polarized femtosecond laser, the periodic nanograting structure on the ablation crater surface was formed . The periodicity is much less than the laser wavelength. The direction of nanograting alignment depends on the polarization laser beam. Micro-Raman spectra show that the intensity of Eg Raman vibrating mode of rutile phase increases and that of Alg Raman vibrating mode decreases apparently within the ablation crater. With the increase of irradiation time and laser average power, the Raman vibrating modes of anatase phase emerged. Rutile phase of TiO2 single crystal is partly transformed into anatase phase.
In this paper, TitaiJum dioxide （TiO2） rutile single crystal was irradiated by infrared femtosecond laser pulses with repetition rate of 250 kHz. For a P-polarized femtosecond laser, the periodic nanograting structure on the ablation crater surface was formed . The periodicity is much less than the laser wavelength. The direction of nanograting alignment depends on the polarization laser beam. Micro-Raman spectra show that the intensity of Eg Raman vibrating mode of rutile phase increases and that of Alg Raman vibrating mode decreases apparently within the ablation crater. With the increase of irradiation time and laser average power, the Raman vibrating modes of anatase phase emerged. Rutile phase of TiO2 single crystal is partly transformed into anatase phase.
基金
Project supported by Shanghai Leading Academic Discipline Project, China （Grant No T0104）, the Shanghai Nano-technology Promotion Center and Science ＆ Technology of Shanghai Municipality, China （Grant No 0652nm005）, Science Foundation of Shanghai Municipal Commission Education and Science and Technology Commission of Shanghai Municipal, China （Grant No 06PJ14042）.