摘要
研究了１４２０铝锂合金在２种不同应力比（０．１和０．７）下的疲劳长裂纹扩展特性和闭合效应，测量了裂纹扩展的门槛值和闭合力．虽然１４２０合金具有较低的本征门槛值，然而在低应力比下却呈现出优良的疲劳裂纹扩展特性，表现在低应力比下较高的疲劳门槛值和近门槛区裂纹扩展的自抑制．从实验的角度探讨了该合金“自抑制”现象产生的原因，指出这种作用主要来源于外韧化作用。
The long crack propagation properties for a Russian aluminum lithium alloy (1420) were investigated at a stress ratio of 0 1. The tests at the stress ratio of 0 7 were also carried out in order to obtain the growth rates and effective intensity factor range relation and the intrinsic threshold of the material. The closure levels were measured near threshold region with a compliance technique. The mechanism of crack restraint near threshold and closure effect were discussed.